Braze welding materials for JH series drilling bits are main used in exploit oil, coal, gold and geological prospecting, well drilling, excavating, core bit. These braze welding materials has good invasion property used for constructional steel and hard alloy powder, good wrapping property, sintering property and strength used for monocrystalline diamond and PDC. The matrix must be clean up before welding, the welding temperature can be 30~50 degrees more than liquidus, and make ajustment according to the welding method.
鉆探鉆頭用釬焊料的分類、型號、代號、熔化溫度（表1）
分類
型號
企業代號
通用名
熔化溫度（表1）
銅鎳錳
B-Cu60NiMn
JH-3
1030-1080℃
B-Cu61NiMn
JH-2
102
1150-1200℃
銅鎳錫錳
B-Cu78NiSnMn
JH-5
516
1050-1100℃
銅鎳鋅錳
B-Cu50NiZnMn
JH-1
1050-1120℃
B-Cu58NiZnMn
JH-7
930-980℃
B-Cu70NiZnMn
JH-6
930-970℃
B-Cu55NiZnMn
JH-4
905-940℃
銅鎳鋅錳硅
B-Cu55NiZnMnSi
CX-55
910-930℃
1.2 The classification, grade, code, common name and melting tempreture of braze welding materials used for drilling bits (Tab 1).
Classification
Grade
Code
Common name
Melting tempreture (Tab 1)
Cu,Ni,Mn
B-Cu60NiMn
JH-3
1030-1080℃
B-Cu61NiMn
JH-2
102
1150-1200℃
Cu,Ni,Sn，Mn
B-Cu78NiSnMn
JH-5
516
1050-1100℃
Cu,Ni,Zn，Mn
B-Cu50NiZnMn
JH-1
1050-1120℃
B-Cu58NiZnMn
JH-7
930-980℃
B-Cu70NiZnMn
JH-6
930-970℃
B-Cu55NiZnMn
JH-4
905-940℃
Cu,Ni,Zn，Mn，Si
B-Cu55NiZnMnSi
CX-55
910-930℃
化學成分（表2）
分類
型號
企業代號
化學成分（%）
Cu
Ni
Mn
Zn
Si
Sn
雜質總量
銅鎳錳
B-Cu60NiMn
JH-3
余量
19.0-21.0
19.0-21.0
≤0.2
B-Cu61NiMn
JH-2
余量
26.0-28.0
10.0-12.0
0.6-1.0
≤0.2
銅鎳錫錳
B-Cu78NiSnMn
JH-5
余量
10.0-12.0
5.0-6.5
0.5-1.5
5.5-6.5
≤0.2
銅鎳鋅錳
B-Cu50NiZnMn
JH-1
48.0-51.5
14.0-16.0
23.5-26.5
余量
≤0.2
B-Cu58NiZnMn
JH-7
57.0-59.0
4.0-6.0
3.5-5.5
余量
≤0.2
B-Cu70NiZnMn
JH-6
56.0-72.0
6.8-7.8
14.5-15.5
余量
≤0.2
B-Cu55NiZnMn
JH-4
52.0-55.0
8.0-9.0
5.0-6.0
余量
≤0.2
銅鎳鋅錳硅
B-Cu55NiZnMnSi
CX-55
54.0-56.0
6.0-8.0
4.0-6.0
余量
≤0.2
化學成分應符合上表的規定，如果用戶有特殊要求時，可按供貨合同執行。
1.3 chemical composition （Tab 2）
Classification
Grade
Code
Chemical composition（%）
Cu
Ni
Mn
Zn
Si
Sn
impurity
Cu,Ni,Mn
B-Cu60NiMn
JH-3
Surplus
19.0-21.0
19.0-21.0
≤0.2
B-Cu61NiMn
JH-2
Surplus
26.0-28.0
10.0-12.0
0.6-1.0
≤0.2
Cu,Ni,Sn，Mn
B-Cu78NiSnMn
JH-5
Surplus
10.0-12.0
5.0-6.5
0.5-1.5
5.5-6.5
≤0.2
Cu,Ni,Zn，Mn
B-Cu50NiZnMn
JH-1
48.0-51.5
14.0-16.0
23.5-26.5
Surplus
≤0.2
B-Cu58NiZnMn
JH-7
57.0-59.0
4.0-6.0
3.5-5.5
Surplus
≤0.2
B-Cu70NiZnMn
JH-6
56.0-72.0
6.8-7.8
14.5-15.5
Surplus
≤0.2
B-Cu55NiZnMn
JH-4
52.0-55.0
8.0-9.0
5.0-6.0
Surplus
≤0.2
Cu,Ni,Zn，Mn，Si
B-Cu55NiZnMnSi
CX-55
54.0-56.0
6.0-8.0
4.0-6.0
Surplus
≤0.2
Chemical composition should conforms with the regulations above, we alos can acoording to client's request
1.4 產品供應規格
1.4.1 塊狀釬料規格及允許誤差按以下規定執行（表3）
厚度(mm)
寬度(mm)
長度(mm)
基本尺寸
允許偏差
基本尺寸
允許偏差
基本尺寸
允許偏差
2.5、4、5、6、8、10、12、15
±0.5
10、12、16、20、22、25、30、35、40
±1
10、12、16、20、22、25、30、35、40
±1
1.4 Specification
T(mm)
W(mm)
L(mm)
Size
Allowance
Size
Allowance
Size
Allowance
2.5、4、5、6、8、10、12、15
±0.5
10、12、16、20、22、25、30、35、40
±1
10、12、16、20、22、25、30、35、40
±1
1.4.2 粒狀釬料有1~20毫米各種規格。
1.4.2 Specification of granular braze weling materials is from 1-20mm.
1.4.3 各種型號釬料可按需方要求協商供應其它規格。
1.4.3 Special specification according to client's request.